Pitting type corrosion of inox pipe - Corrosion analysis

Pitting type corrosion of inox pipe - Corrosion analysis

The objective it was to define the corrosion causes 

Starting from visual analysis and classification it proceded by classifying the phenomenon in terms of chemistry and metallurgy of the metal object of defect and analyzing EDS microanalysis the composition of corrosion products on the sites corrosive.

Corrective actions have focused on the choice of inox steel more resistant to pitting corrosion (including the choice of surface finish).


Dott. Luca Giulietti - Corrosionist

Tag: Railways and transportation

Materials Testing Centre

Blade wear

One of the phenomenon that brings a component not to be useful for its purpose, even if it's not broken, is wear, that means "lost" of...
Failure on a polyethylene tank

Failure on a polyethylene tank

The tank to be tested presented a superficial ductile  fracture, with different damaged parts around it. SEM view. Thickness determination....
Food contact suitability - knife with ceramical blade

Food contact suitability - knife with ceramical blade

Failure on a fiberglass pipe

The goal of the investigation is to characterize the material and understand the causes of the damage occured on a fiberglass pipe.
Our team of experts is ready to support you with testing and improvement of materials, products and processesSend us your request
Reserved Area
Store
Tec Star
Corporate Responsability
SIDEIUS: A Brand of TEC Eurolab
Tec Eurolab around the world
Accreditations Aster Accredia Accredia Accredia Tuv Nord Nadcap Crit
Copyright © 2005-2017 TEC Eurolab Srl
Sigla.com - Internet Partner
[ Privacy Policy on website and cookies ]