A casting defect, not detectable at magnifications lower than ten diameters, consisting of interdendritic voids. This defect results from contraction during solidification where there is not an adequate opportunity to supply filler material to compensate for shrinkage. Alloys with a wide range in solidification temperature are particularly susceptible.